CYCLOY - C6200
✔ 장점
✔물성표
※ If the entire table is not visible, you can scroll the table left and right to check the entire table.
TYPICAL PROPERTIES1 | TYPICAL VALUE | UNIT | STANDARD |
---|---|---|---|
MECHANICAL | |||
Tensile Str, yld, Type I, 50 mm/min | 67 | MPa | ASTM D 638 |
Tensile Elong, brk Type I, 50 mm/min | 50 | % | ASTM D 638 |
Flex Stress, yld, 2.6 mm/min, 100 mm span | 103 | Mpa | ASTM D 790 |
Flex Mod, 2.6 mm/min, 100 mm span | 2690 | Mpa | ASTM D 790 |
IMPACT | |||
Izod Impact notched, 23℃ | 534 | J/m | ASTM D 256 |
Instrumented Impact Energy @ peak, 23℃ | 61 | J | ASTM D 3763 |
Instrumented Impact Energy @ peak, -30℃ | 54 | J | ASTM D 3763 |
THERMAL | |||
HDT, 1.84 Mpa, 3.2 mm, unannealed | 88 | ℃ | ASTM D 648 |
HDT, 1.82 Mpa, 6.4 mm, unannealed | 91 | ℃ | ASTM D 648 |
Relative Temp Index, Elec | 85 | ℃ | UL 746B |
Relative Temp Index, w/impact | 85 | ℃ | UL 746B |
Relative Temp Index, Mech w/o impact | 85 | ℃ | UL 746B |
PHYSICAL | |||
Specific Gravity | 1.18 | - | ASTM D 792 |
Mold Shrinkage flow, 3.2 mm | 0.4-0.6 | % | ASTM D 955 |
Mold Shrinkage, xflow, 3.2 mm | 0.4-0.6 | % | ASTM D 955 |
Melt Flow Rate, 260℃/2.16kgf | 14.5 | g/10 min | ASTM D 1238 |
Spiral Flow, 260℃,10 ips, 3.175 X 1524 mm | 685.8 | mm | - |
ELECTRIAL | |||
Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D 495 |
Hot Wire Ignition {PLC} | 2 | PLC Code | UL 746A |
High Voltage Arc Track Rate {PLC} | 3 | PLC Code | UL 746A |
High Ampere Arc Ign, surface {PLC} | 0 | PLC Code | UL 746A |
Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A |
Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 |
Surface Resistivity, ROA | >1.E+15 | cm | IEC 60093 |
Dielectric Strength, in oil, 0.8 mm | 35 | kV/mm | IEC 60243-1 |
Dielectric Strength, in oil, 1.6 mm | 25 | kV/mm | IEC 60243-1 |
Dielectric Strength, in oil, 3.2 mm | 17 | kV/mm | IEC 60243-1 |
TYPICAL PROPERTIES1 | TYPICAL VALUE | UNIT | STANDARD |
---|---|---|---|
Relative Permittivity, 50/60 Hz | 2.8 | - | IEC 60250 |
Relative Permittivity, 1 MHz | 2.7 | - | IEC 60250 |
Dissipation Factor, 50/60 Hz | 0.004 | - | IEC 60250 |
Dissipation Factor, 1 MHz | 0.008 | - | IEC 60250 |
Flame Characteristics | |||
UL Recognized, 94HB Flame Class Rating (3) | 0.7 | mm | UL 94 |
UL Recognized, 94V-1 Flame Class Rating (3) | 1.2 | mm | UL 94 |
UL Recognized, 94V-0 Flame Class Rating (3) | 1.5 | mm | UL 94 |
UL Recognized, 94-5VA Rating (3) | 3.4 | mm | UL 94 |
UL Recognized, 94-5VB Rating (3) | 2 | mm | UL 94 |
CSA (see File for Complete listing) | LS88480 | File No. | CSA LISTED |
PROCESSNG PARAMETERS | TYPICAL VALUE | UNIT |
---|---|---|
Injection Molding | - | - |
perature | 80-90 | ℃ |
Drying Time | 03월 04일 | hrs |
Drying Time (Cumulative) | 0.04 | % |
Melt Temperature | 245-275 | ℃ |
Nozzle Temperature | 245-275 | ℃ |
Front-Zone 3 Temperature | 245-275 | ℃ |
Middle-Zone 2 Temperature | 220-265 | ℃ |
Rear-Zone1 Temperature | 220-255 | ℃ |
Mold Temperature | 60-80 | ℃ |
Back Pressure | 0.3-0.7 | Mpa |
Screw Speed | 40-70 | rpm |
Shot to Cylinder Size | 30-80 | % |
Vent Depth | 0.038-0.076 | mm |